 Post subject: Faceting Stibiotantalite
PostPosted: Fri Nov 18, 2022 4:18 pm 
Offline
New to the Forum or The Quiet Type

Joined: Wed Sep 28, 2022 4:45 am
Posts: 1
Hi I wanted to know if there were any tips to faceting Stibiotantalite, I know it is heat sensitive so to be careful with the dop. Thanks Max


Top
 Profile  
Reply with quote  
 Post subject: Re: Faceting Stibiotantalite
PostPosted: Tue Nov 22, 2022 1:19 am 
Offline
Gold Member
User avatar

Joined: Tue Apr 05, 2016 7:58 pm
Posts: 1424
Location: San Marcos, CA
Looks challenging based on cleavage. Keep us posted on your adventure if you would.

_________________
The Gem Garden
San Marcos, CA


Top
 Profile  
Reply with quote  
 Post subject: Re: Faceting Stibiotantalite
PostPosted: Tue Nov 22, 2022 3:13 am 
Offline
Gemology Online Veteran
User avatar

Joined: Sat May 22, 2010 2:51 am
Posts: 755
Location: South Africa
Vargas (1969:307) wrote "Heat sensitivity - moderate [...] This is fairly easy material to handle if proper precautions are taken. The cleavages are not very troublesome. Polishing is fairly easy." They recommend Linde A (AlOx) on tin or tin/lead (use Batt).


Top
 Profile  
Reply with quote  
 Post subject: Re: Faceting Stibiotantalite
PostPosted: Tue Nov 22, 2022 5:10 pm 
Offline
Gold Member
User avatar

Joined: Tue Apr 05, 2016 7:58 pm
Posts: 1424
Location: San Marcos, CA
Gem Cutting, Sinkankas 1955, 1962 page 282

"Somewhat heat sensitive, dop cautiously. Laps easily and smoothly, polishes well on tin with Linde-A. Differences noted in speed of grinding, direction parallel to the broad face of the crystal being softer than other directions. Crown angles 30° - 40°; pavilion angles 37° - 40°; cut shallow because of dark color and high refractive index."

Sinkankas has a very similar opinion as Vargs on this mineral, I have personally never cut any. I would note that Linde-A has not been around for many years as Union Carbide went out of buisness a long time ago. Probably any good grade aluminum oxide would produce a good result.

_________________
The Gem Garden
San Marcos, CA


Top
 Profile  
Reply with quote  
 Post subject: Re: Faceting Stibiotantalite
PostPosted: Fri Nov 25, 2022 6:25 pm 
Offline
Established Member

Joined: Sun Mar 18, 2007 1:04 am
Posts: 35
Location: Central New Mexico
Union Carbide is wholly owned by Dow Chemical since 2001. Still in business however, as is it's former Linde division that was spun off as Praxair in the 1990's. Looking at Praxair's website, Linde A is still produced. Perhaps it is simply not available at the retail level?

https://www.praxairsurfacetechnologies. ... uspensions

Ironically, Praxair and the European version of Linde recombined in 2018 after 101 years of separation - Linde's US holdings were sold to UC during WWI.

I don't think I've ever used Linde A - as you say, any good alumina does just fine in it's place.


Top
 Profile  
Reply with quote  
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 5 posts ] 

All times are UTC - 4 hours


Who is online

Users browsing this forum: vistagrande and 24 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  
Powered by phpBB © 2000, 2002, 2005, 2007 phpBB Group
Gemology Style ported to phpBB3 by Christian Bullock